316H/S31609/SUS 316 Stainless Steel
Alloy 316H (UNS S31609) is a high carbon modification of Alloy 316 developed for use in elevated temperature service. The alloy has higher strength at elevated temperatures and is used for structural and pressure vessel applications at temperatures above 932°F (500°C). The higher carbon content of 316H also delivers higher tensile and yield strength than 316/316L and its austenitic structure provides excellent toughness down to cryogenic temperatures.
The corrosion resistance of Alloy 316H is comparable to Alloy316/316L and is superior to Alloy 304/304L in moderately corrosive environments. It is often used in process streams containing chlorides or halides. The alloy resists atmospheric corrosion, as well as, moderately oxidizing and reducing environments. It also resists corrosion in polluted marine conditions.
Alloy 316H is non-magnetic in the annealed condition. It cannot be hardened by heat treatment, however the material will harden due to cold working. It can be easily welded and processed by standard shop fabrication practices.
STANDARDS
INDUSTEEL TRADEMARKS
UNS
ASTM
EURONORMS EN
SUS
316H
S31609
316H
1.4919
SUS 316
Chemical Composition:
Grade
C
Mn
Si
P
S
Cr
Mo
Ni
N
316 H
min.
max.
0.04
0.10
–
2.0
–
0.75
–
0.045
–
0.03
16.0
18.0
2.00
3.00
10.0
14.0
0.1
Mechanical Properties
Grade
Tensile Strength (MPa) min
Yield Strength 0.2% Proof (MPa) min
Elongation (% in 50mm) min
Hardness
Rockwell B (HR B) max
Brinell (HB) max
316 H
515
205
40
95
217
Physical Properties
Grade
Density (kg/m3)
Elastic Modulus (GPa)
Mean Coefficient of Thermal Expansion (μm/m/°C)
Thermal Conductivity (W/m.K)
Specific Heat 0-100°C (J/kg.K)
Electrical Resistivity (nΩ.m)
0-100°C
0-315°C
0-538°C
at 100°C
at 500°C
316 H
8000
193
15.9
16.2
17.5
16.3
21.5
500
740
Product details:
Thickness
3.0 mm-30.0 mm or as customized
Steel Grades
AISI316H
Application
Medical equipment, Food industry
Production
Hot-Rolled
Standard
ASTM A240/A480
Width
1000 mm, 1250 mm, 1500 mm, 2000 mm or as customized