Hastelloy B/UNS N10001 sheet/bar/pipe
Description
alloy Hastelloy B/B2, the carbon and silicon content is extremely low, reducing the HAZ carbon and other impurities precipitation, so the weld has sufficient corrosion resistance.
Alloy Hastelloy B/B2 in the reduction of medium with very good corrosion resistance, such as a various temperature and concentration of hydrochloric acid. In the middle of the concentration of sulfuric acid solution (or contain a certain amount of chloride ions) also has very good corrosion resistance. At the same time Hastelloy B/B2 can be used to acetic acid and phosphoric acid environment.
Hastelloy B/B2 Specifications
Grade
UNS
W.Nr
Hastelloy B
N10001
2.4810
Hastelloy B2
N10665
2.4617
Hastelloy B/B2 Chemical Composition
Grade
%
Ni
Mo
Fe
Cr
Co
C
Mn
V
Si
P
S
Hastelloy B
Min.
Bal
26
4
0.2
Max.
30
6
1
2.5
0.05
1
0.4
1
0.04
0.03
Hastelloy B-2
Min.
Bal
26
2
Max.
30
7
1
1
0.02
1
0.1
0.04
0.03
Hastelloy B/B2 Mechanical properties:(Minimum value at 20℃)
Grade
Tensile Strength
σb/MPa
Yield Strength
σp0.2/MPa
Elongation
σ5 /%
Hastelloy B/B2
≥690
≥310
≥40
Hastelloy B/B2 Standards
Bar
Forging
Sheet/Strip
Pipe
ASTM B335
ASTM B564
ASTM B333
ASTM B906
ASTM B622
ASTM B619
ASTM B775
ASTM B751
Hastelloy B/B2 Size Range
Wire: Dia 0.08-12mm
Bar: Dia1.0-300mm
Strip(Coil): 0.2-20mm TCK x 10-300mm W
Sheet: min.0.7mm TCK x 1200mm W max.
Tube & Forging & Machine Parts: customized
Welding wire: 0.8mm,1.0mm,1.2mm,2.0mm,2.4mm,3.2mm,3.8mm,4.0mm etc
Welding Strip: 0.4-0.7mm TCK x 25-60mm W