Nickel 201
Standard Grade
Trade Name
UNS No.
DIN
BS
JIS
GB/T
Nickel 201
UNS N02201
LC-Ni99
(2.4068)
NA12
NW2201
Ni99.0-LC
N5
Specification
ASTM B161, ASTM B 163, ASME SB 163, ASTM B 725, ASME SB 725, ASTM B 730, ASME SB 730, DIN 17751, BS3074, JIS H 4552, WS 2.4068, GB/T2882
Typical use Typical use
Alloy 201 (UNS N02201) is a commercially pure wrought nickel, with good mechanical properties and an excellent resistance to many corrosives. Nickel 201 has low carbon (0.02% max) for applications over 315°C it is mainly used for food processing equipment, chemical shipping drums, caustic handling equipment and piping, electronic parts, aerospace and missile components, rocket motor cases, magnetostrictive devices.
Weight Formula
Average Wall: (OD-WT) x WT x 0,0280 = Kg/m (all sizes in mm)
Minimum Wall: (OD-WT) x WT x 0,0291 = Kg/m (all sizes in mm)
Technical Data Sheet
Chemical Composition Limits
Weight%
Ni
Cu
Fe
Mn
C
Si
S
Nickel Alloy 200
99.0 min
0.25 max
0.40 max
0.35 max
0.02 max
0.35 max
0.01 max
Typical Mechanical Properties
Material
Tensile Strength
Yield Strength (0.2% Offset)
Elongation in 2" (%)
Hardness
ksi
MPa
ksi
MPa
Rockwell B
Nickel 200
55-75
380-520
15-30
105-210
55-40
62 max
Nominal Results for Cold Rolled, Annealed Rod and Bar.
Availability
Nickel 201 (UNS N02201) is available in Bar, Rods, Tube, Pipe, Plate, Sheet, Strip, Wire and Forging Stock. For further information please contact Sales.