Oxygen Free Copper Tube-C10200
Oxygen Free Copper Tube-C10200- is produced by the direct conversion of selected refined cathodes and castings under carefully controlled anaerobic conditions to prevent any contamination of pure, oxygen-free metal during processing. Characteristics of oxygen-free copper are high electrical and thermal, high ductility, ease of welding, high impact strength, and low volatility under high vacuum.
Standard Grade
ASTM B 111
C10200
DIN
OF-Cu2
0040
BS 2871
C102
JIS H3300
C1020
GB/T 5231
TU3
Cu
99.95 min
99.99 min
99.90 min
99.96 min
99.95 min
O
10 ppm max
5ppm max
10 ppm max
Lead
0.005
Bi
0.0025
Total impurities
0.04
Condition
H55
R200
O
O
M
H80
R220
M
OL
M2
R240
1/2 H
Y2
-
R290
H
Y
R360
Yield Strength
N/mm2
205 min
100 max
275 min
140 max
-
180 min
250 min
320 min
Tensile Strength
N/mm2
250 min.
200-250
200-250
205min
200 min
310 min.
220-260
270 min
205 min
220 min
240-300
245-325
250 min
290-360
315 min
290 min
360 min
Elongation (%)
Min -/42
40
40
Min 33-42
-
40
Min 8/15
Min 4/6
Min 2
Hardness Hv5
40-65
60max
HR15T: 60max
40-65
40-65
100 min
HR15T: 65max
45-75
65-95
HR30T: 30-60
70-100
90-110
HR30T: 55 min
-
Min 119
-
Typical use
OFHC/OFE COPPER TUBE APPLICATIONS
Electrical & Electronic Conductors
Superconductor matrimes
Vacuum tubes
Glass-to-metal seals
Power Substations
Weight Formula
Average Wall: (OD-WT) x WT x 0,0284= Kg/m (all sizes in mm)
Minimum Wall: (OD-WT) x WT x 0,0295 = Kg/m (all sizes in mm)