304 Cold Rolled Stainless Steel Coil
Grade 304 is the most versatile and most widely used stainless steel, available in a wider range of products, forms and finishes than any other. It has excellent forming and welding characteristics. Which is eadily brake or roll formed into a variety of components for applications in the industrial, architectural, and transportation fields.
Grade 304 also has outstanding welding characteristics. Post-weld annealing is not required when welding thin sections.
Grade |
304 stainless steel coil |
|
Thinckness |
0.3-6mm |
|
Tolerance |
+/-0.02mm |
|
Widthness |
1000mm, 1219mm, 1524mm or as customized |
|
Length |
Coil |
|
Brand name |
TISCO,BAO Steel,ZPSS,LISCO,BAO XIN... |
|
Standard |
JIS, AISI, ASTM, GB, DIN, EN ,etc. |
|
Finish |
2B, Hairline, No.4, BA, 8K mirror, etc. |
|
Application |
kitchen cabinet, industry material, Food processing equipment, particularly in beer brewing, milk processing, and wine making |
|
Certification |
SGS |
|
Packaging |
Standard exporting packing; seaworthy package. |
|
MOQ |
2 Tons |
|
Price time |
FOB, CFR, CIF, CNF |
|
Delivery time |
Within 15-20 working days after receiving your deposit |
|
Payment |
30% T/T in advanced+70% balanced; irrevocable L/C at sight |
|
Remarks |
Insurance is all risks and accept the third party test |
304 |
C |
Si |
Mn |
P |
S |
Ni |
Cr |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.045 |
≤0.03 |
8.00~12.00 |
18.00~20.00 |
MECHANICAL PROPERTY
304 |
Tensile Strength: |
σb (MPa)≥520 |
Yield strength : |
σ.2 (MPa)≥205 |
|
Elongation: |
δ5 (%)≥40 |
|
Hardness : |
≤187HB;≤90HRB;≤200HV |
|
Density : |
7.93g/cm3 |
|
specific heat capacity |
c(20℃)0.502 J·(g·C)-1 |
|
heat conductivity |
λ/W(m·℃)-1 |
|
melting point |
1398~1420℃ |
|
304 |
Tensile Strength: |
σb (MPa)≥520 |
Yield strength : |
σ0.2 (MPa)≥205 |
|
Elongation: |
δ5 (%)≥40 |
|
Hardness : |
≤187HB;≤90HRB;≤200HV |
APPLICATIONS
304 stainless steel has many applications, which is wildely used in the fields of kitchen cabinet, industry material, water heater, food industry,sinks, utensils.