Introduction
304L stainless steel is a kind of general low carbon stainless steel, it is widely used to make for a good comprehensive performance, corrosion resistance ,form-ability of equipment and parts.
It has corrosion resistance and good heat resistance, low temperature resistance and good mechanical properties. No heat treatment hardening phenomenon (non-magnetic, using temperature to -196 ℃ ~ 800 ℃).
Applied to the grain boundary corrosion resistant requirements of high chemical industry, coal, oil field open machine, building materials with heat-resistant parts and heat treatment which are difficult parts.
Technical Parameter
304L stainless steel
|
Standard
|
Grade
|
Chemical Composition
%
|
Temper
|
Yied strength
Mpa
|
Tensile strength
Mpa
|
Elongation %
|
Hardness
|
GB
|
00Cr19Ni10
|
C≤0.030,Mn≤2.00,
Si≤1.00,P≤0.045,
S≤0.030,Cr 18.0~20.0,
Ni 8~12
|
Annealed,
hot rolled/
cold rolled
|
≥170
|
≥480
|
≥40
|
HV≤200
|
USA
|
304L
|
JIS
|
SUS304L
|
German
|
1.4306
|
Stainless Steel Angle Bar
Stainless steel angel bar is perpendicular to each other on both sides of the strip into angular steel.
Stainless steel angel bar composed of various components of the force, but also for connections between components. Widely used in various building structures and engineering structures such as bridges, transmission towers, hoisting and conveying machinery, ships, industrial furnace, reaction tower, container frame and warehouse shelves.
Application
304L,It belongs to the Austenitic steel,which is applied to the grain boundary corrosion resistant requirements of high chemical industry, coal, oil field open machine, building materials with heat-resistant parts and heat treatment which are difficult parts.
Metal structures, Architectural applications, Food industry, chemical and oil industry, pharmaceutical industry, nuclear industry, Naval industry, non-magnetic constructions, cryogenic service, high temperature service application Steel type: 304, 316 304L 316L