Introduction
316L stainless Steel adds Mo (2-3%), so it has excellent corrosion resistance and high temperature strength; SUS316L carbon content is lower than SUS316, therefore, the resistance to inter-granular corrosion resistance is better than SUS316: high temperature creep strength is high. It can be used in harsh conditions.good strain hardening and non-magnetic.
1) cold-rolled product appearance, good gloss, beautiful;
2) the addition of Mo, corrosion resistance, especially resistance to pitting corrosion;
3) excellent high temperature strength
4) Excellent hardening (after processing weakly magnetic)
5) solid solution state non-magnetic;
6) relative to 304 stainless steel, it has higher prices.(10Ni)

Welding
Excellent weldability by all standard fusion and resistance methods, both with and without filler metals. Heavy welded sections in Grade 316 require post-weld annealing for maximum corrosion resistance. This is not required for 316L.
316L stainless steel is not generally weldable using oxyacetylene welding methods.

Machining
316L stainless steel tends to work harden if machined too quickly. For this reason low speeds and constant feed rates are recommended.
316L stainless steel is also easier to machine compared to 316 stainless steel due its lower carbon content.

Hot and Cold Working
316L stainless steel can be hot worked using most common hot working techniques. Optimal hot working temperatures should be in the range 1150-1260°C, and certainly should not be less than 930°C. Post work annealing should be carried out to induce maximum corrosion resistance.
Most common cold working operations such as shearing, drawing and stamping can be performed on 316L stainless steel. Post work annealing should be carried out to remove internal stresses.

Hardening and Work Hardening
316L stainless steel does not harden in response to heat treatments. It can be hardened by cold working, which can also result in increased strength.

Technical Parameter

316L stainless steel
Standard	Grade	Chemical Composition %	Technique	Yied strength Mpa	Tensile strength Mpa	Elongation %	Hardness
GB	00Cr17Ni14M02	C≤0.030，Mn≤2.00， Si≤1.00，P≤0.045， S≤0.030，Cr 16.0~18.0, Ni 10.0~14.0，Mo 2.00~3.00	cold /hot rolled	≥177	≥485	≥40	HV≤200
USA	316L
JIS	SUS316L
German	1.4435

Stainless Steel Angle Bar
Stainless steel angel bar is perpendicular to each other on both sides of the strip into angular steel.

Stainless steel angel bar composed of various components of the force, but also for connections between components. Widely used in various building structures and engineering structures such as bridges, transmission towers, hoisting and conveying machinery, ships, industrial furnace, reaction tower, container frame and warehouse shelves.

Application
316L is suitable for mixing equipment, chemicals, fuels, papermaking, oxalic acid, waste production equipment, photography, food industry, coastal facilities., ect.
Our cold rolled coil and sheet are a very popular choice for applications from consumer goods and prestigious building to corrosion,resistantfor the process industry.
Hot rolled coil and sheet are used in application such as the production of process plant equipment and a host of other application.