Introduction
2205 duplex stainless steel standard: ASTM A240/A240M--01 chromium 2205 duplex stainless steel alloy is a 22%, 2.5% 4.5%-NI-n alloy composition Mo and duplex stainless steels. It has high strength, good toughness and good global and local resistance to stress corrosion.
2205 duplex stainless steel yield strength of austenitic stainless steel is twice times, this feature enables designers to design products reduce the weight, price advantage over the 316,317L. This alloy is suitable within the temperature range-50 ° F/600 ° f. Exceeding this temperature range of application, this alloy can also be considered, but there are some limitations, especially when applied to welded structures.

Corrosion Resistance
Grade 2205 stainless steel exhibits excellent corrosion resistance, much higher than that of grade 316. It resists localized corrosion types like intergranular, crevice and pitting. The CPT of this type of stainless steel is around 35°C. This grade is resistant to chloride stress corrosion cracking (SCC) at temperatures of 150°C. Grade 2205 stainless steels are apt replacements to austenitic grades, especially in premature failure environments and marine environments.

Heat Resistance
The high oxidation resistance property of Grade 2205 is marred by its embrittlement above 300°C. This embrittlement can be modified by a full solution annealing treatment. This grade performs well at temperatures below 300°C.

Heat Treatment
The best suited heat treatment for this grade is solution treatment (annealing), between 1020 - 1100°C, followed by rapid cooling. Grade 2205 can be work hardened but cannot be hardened by thermal methods.

Welding
Most standard welding methods suit this grade, except welding without filler metals, which results in excess ferrite. AS 1554.6 pre-qualifies welding for 2205 with 2209 rods or electrodes so that the deposited metal has the right balanced duplex structure.
Adding nitrogen to the shielding gas ensures that adequate austenite is added to the structure. The heat input must be maintained at a low level, and the use of pre or post heat must be avoided. The co-efficient of thermal expansion for this grade is low; hence the distortion and stresses are lesser than that in austenite grades.

Machining
The machinability of this grade is low due to its high strength. The cutting speeds are almost 20% lower than that of grade 304.

Fabrication
The fabrication of this grade is also affected by its strength. Bending and forming of this grade requires equipment with larger capacity. Ductility of grade 2205 is lesser than austenitic grades; therefore, cold heading is not possible on this grade. In order to carry out cold heading operations on this grade, intermediate annealing should be carried out.

Technical Parameter

2205 stainless steel
Standard	Grade	Chemical Composition %	Technique	Yied strength Mpa	Tensile strength Mpa	Elongation %	Hardness
GB	00Cr24Ni6M03N	C≤0.03，Mn≤2.00， Si≤1.00，P≤0.030， S≤0.020，Cr 21.0~23.0, Ni 4.5~6.5,Mo 2.5~3.5, N 0.08~0.20	Annealed, cold rolled	≥450	≥620	≥18	HV≤320
USA	S31803/S32205
JIS	SUS329J3L
German	1.4462

Specification	Thickness:0.3-6.0mm 3.0mm*100mm
	Width:500-2000mm normal size1000 1219 1220 1240 1250 1500 2000mm
	Length:1000-6000mm normal size 2438 2440 3000 6000mm
Mill	TISCO BAOSTEEL LISCO BAOXIN ZPSS JISCO
Finish	2b/No.1
Edge	Mill /raw or slit edge
Weight	ThicknessXWidthXLengthX7.93(304) /7.98(316L)per sheet
Technique	cold rolled hot rolled
Payment term	30% T/T in advance,the balance before shipment 30% T/T in advance,the balance L/C at sight 100% L/C at sight
Packing	1.Export sea worthy package + water proof paper + wooden pallet 2.Max Loading 25mt for each 20GP container 3.Safe loading and fixing Professional Teams
Delivery time	Within 7-10 working days after received 30%T/T of deposit or L/C original
Trade terms	FOB SHANGHAI CFR&CIF your port
Quality control	Mill Test Certificate is supplied with shipment
Application	1.Construction field, shipping building industry 2. Petroleum and Chemical Industries 3.Food and Mechanical Industries

Cold-rolled plate
1. Stretch good, toughness, but the price is more expensive;
2. Cold rolling processing surface without oxide skin, good quality;
3. Cold rolling is generally used in the production of strip, the rolling speed is high;
4. Cold rolling than the thickness of the high precision. Mechanical properties, surface and so on in the hot rolling;
5. Cold-rolled steel plate due to a certain degree of work hardening, low toughness, but can achieve better yield ratio, used for cold-formed spring and other parts;
6. Cold plate yield point closer to the tensile strength, so the use of risk in the process of no predictability, when the load exceeds the allowable load prone to accidents
7. The surface of the cold rolling plate without plating is gray.
8. Cold rolling plate plating surface smoothness is higher than the hot plate.

Application
* Pressure vessel and high pressure storage tanks, high pressure piping, heat exchangers (chemical process industries).
* Oil and gas pipelines, heat ex-changer pipe.Sewage treatment systems.
* Classifier, bleaching of pulp and paper industry equipment, storage systems.
* Ship or truck cargo box
* Food processing equipment