Introduction
316 stainless steel, 06 cr17ni12mo2 (old version 0 cr17ni12mo2, S31608) by adding Mo, its corrosion resistance, resistance to atmospheric corrosion and high temperature strength are particularly good, and it can be used in critical conditions. Excellent work hardening (non-magnetic).
Corrosion resistance, heat resistance, heat treatment, welding

Technical Parameter

316 stainless steel
Standard	Grade	Chemical Composition %	Technique	Yied strength Mpa	Tensile strength Mpa	Elongation %	Hardness
GB	0Cr17Ni12M02	C≤0.08，Mn≤2.00， Si≤1.00，P≤0.045， S≤0.030，Cr 16.0~18.0, Ni 10.0~14.0，Mo 2.00~3.00	Annealed, cold rolled	≥205	≥520	≥40	HV≤200
USA	316
JIS	SUS316
German	1.4401

Specification	Thickness:0.3-6.0mm
	Width:500-2000mm normal size1000 1219 1220 1240 1250 1500 2000mm
	Length:1000-6000mm normal size 2438 2440 3000 6000mm
Mill	TISCO
Finish	2b
Edge	Mill /raw or slit edge
Weight	ThicknessXWidthXLengthX7.98 per sheet
Technique	cold rolled
Payment term	30% T/T in advance,the balance before shipment 30% T/T in advance,the balance L/C at sight 100% L/C at sight
Packing	1.Export sea worthy package + water proof paper + wooden pallet 2.Max Loading 25mt for each 20GP container 3.Safe loading and fixing Professional Teams
Delivery time	Within 7-10 working days after received 30%T/T of deposit or L/C original
Trade terms	FOB SHANGHAI CFR&CIF your port
Quality control	Mill Test Certificate is supplied with shipment
Application	1.Construction field, shipping building industry 2. Petroleum and Chemical Industries 3.Food and Mechanical Industries

Cold-rolled plate
1. Stretch good, toughness, but the price is more expensive;
2. Cold rolling processing surface without oxide skin, good quality;
3. Cold rolling is generally used in the production of strip, the rolling speed is high;
4. Cold rolling than the thickness of the high precision. Mechanical properties, surface and so on in the hot rolling;
5. Cold-rolled steel plate due to a certain degree of work hardening, low toughness, but can achieve better yield ratio, used for cold-formed spring and other parts;
6. Cold plate yield point closer to the tensile strength, so the use of risk in the process of no predictability, when the load exceeds the allowable load prone to accidents
7. The surface of the cold rolling plate without plating is gray.
8. Cold rolling plate plating surface smoothness is higher than the hot plate.

Application
316 Pulp and paper equipment heat exchanger, dyeing equipment, film processing equipment, pipelines, coastal areas with material outside the building.Also in the field of electromagnetic valve, mainly used for the shell, clamp, sphere, valve body, valve seat, nut, stem and so on.