Introduction
316L stainless Steel adds Mo (2-3%), so it has excellent corrosion resistance and high temperature strength; SUS316L carbon content is lower than SUS316, therefore, the resistance to inter-granular corrosion resistance is better than SUS316: high temperature creep strength is high. It can be used in harsh conditions.good strain hardening and non-magnetic.
1) cold-rolled product appearance, good gloss, beautiful;
2) the addition of Mo, corrosion resistance, especially resistance to pitting corrosion;
3) excellent high temperature strength
4) Excellent hardening (after processing weakly magnetic)
5) solid solution state non-magnetic;
6) relative to 304 stainless steel, it has higher prices.(10Ni)

Welding
Excellent weldability by all standard fusion and resistance methods, both with and without filler metals. Heavy welded sections in Grade 316 require post-weld annealing for maximum corrosion resistance. This is not required for 316L.
316L stainless steel is not generally weldable using oxyacetylene welding methods.

Machining
316L stainless steel tends to work harden if machined too quickly. For this reason low speeds and constant feed rates are recommended.
316L stainless steel is also easier to machine compared to 316 stainless steel due its lower carbon content.

Hot and Cold Working
316L stainless steel can be hot worked using most common hot working techniques. Optimal hot working temperatures should be in the range 1150-1260°C, and certainly should not be less than 930°C. Post work annealing should be carried out to induce maximum corrosion resistance.
Most common cold working operations such as shearing, drawing and stamping can be performed on 316L stainless steel. Post work annealing should be carried out to remove internal stresses.

Hardening and Work Hardening
316L stainless steel does not harden in response to heat treatments. It can be hardened by cold working, which can also result in increased strength.

Technical Parameter

316L stainless steel
Standard	Grade	Chemical Composition %	Technique	Yied strength Mpa	Tensile strength Mpa	Elongation %	Hardness
GB	00Cr17Ni 14M02	C≤0.030，Mn≤2.00， Si≤1.00，P≤0.045， S≤0.030，Cr 16.0~18.0, Ni 10.0~14.0，Mo 2.00~3.00	cold rolled	≥177	≥485	≥40	HV≤200
USA	316L
JIS	SUS316L
German	1.4435

Specification	Thickness:0.3-6.0mm
	Width:500-2000mm normal size1000 1219 1220 1240 1250 1500 2000mm
	Length:1000-6000mm normal size 2438 2440 3000 6000mm
Mill	TISCO
Finish	2b
Edge	Mill /raw or slit edge
Weight	ThicknessXWidthXLengthX7.93(304) /7.98(316L)per sheet
Technique	cold rolled hot rolled
Payment term	30% T/T in advance,the balance before shipment 30% T/T in advance,the balance L/C at sight 100% L/C at sight
Packing	1.Export sea worthy package + water proof paper + wooden pallet 2.Max Loading 25mt for each 20GP container 3.Safe loading and fixing Professional Teams
Delivery time	Within 7-10 working days after received 30%T/T of deposit or L/C original
Trade terms	FOB SHANGHAI CFR&CIF your port
Quality control	Mill Test Certificate is supplied with shipment
Application	1.Construction field, shipping building industry 2. Petroleum and Chemical Industries 3.Food and Mechanical Industries

Cold-rolled plate
1. Stretch good, toughness, but the price is more expensive;
2. Cold rolling processing surface without oxide skin, good quality;
3. Cold rolling is generally used in the production of strip, the rolling speed is high;
4. Cold rolling than the thickness of the high precision. Mechanical properties, surface and so on in the hot rolling;
5. Cold-rolled steel plate due to a certain degree of work hardening, low toughness, but can achieve better yield ratio, used for cold-formed spring and other parts;
6. Cold plate yield point closer to the tensile strength, so the use of risk in the process of no predictability, when the load exceeds the allowable load prone to accidents
7. The surface of the cold rolling plate without plating is gray.
8. Cold rolling plate plating surface smoothness is higher than the hot plate.

Application
316L is suitable for mixing equipment, chemicals, fuels, papermaking, oxalic acid, waste production equipment, photography, food industry, coastal facilities., ect.
Our cold rolled coil and sheet are a very popular choice for applications from consumer goods and prestigious building to corrosion,resistantfor the process industry.