1050 carbon tool steel
Finkl 1050 carbon tool steel is a medium carbon high strength carbon structural steel, quenched with high strength and hardness, the steel can be machinable medium, heat treatment without temper brittleness, in normalizing or quenching and tempering, Or high-frequency surface hardening and other heat treatment. Fencor Finkl 1050 carbon tool steel can be hardened to HRC42 ~ 46. So if you need the surface hardness, but also want to play 1050 steel superior mechanical properties, often 1050 steel surface carburizing quenching, so you can get the required surface hardness.
Processing:
Shaft parts of the rough: shaft parts according to the use of requirements, production types, equipment conditions and structure, the choice of bar, forgings and other blank form. For the diameter of the outer diameter of the shaft is not the main difference, the general bar to the main; and for the outer diameter of the large difference between the step shaft or important shaft, often use forging, which saves material and reduce the workload of machining, but also Improve mechanical properties. According to the different scale of production, rough forging for free forging and forging two. Small and medium-sized production more free forging, a large number of large-scale production using forging. The following are the same as the "
Shaft parts of the material: shaft parts should be based on different working conditions and the use of different requirements and the use of different heat treatment specifications (such as quenching and tempering, quenching, etc.) to obtain a certain strength, toughness and wear Sex. Fencrole 1050 steel is a common material for shaft parts, it is cheap after quenching and tempering (or normalizing), can get better cutting performance, and can get a higher strength and toughness and other comprehensive mechanical properties, quenched surface Hardness up to 45 ~ 52HRC.
Metallographic organization: pearlite + ferrite.
US Fencor Finkl 1050 carbon tool steel, using electric furnace, flat furnace or pure oxygen converter steelmaking made of the whole static steel, with the characteristics of uniform microstructure. The steel has a carbon content of 0.4%, excellent wear resistance, reduced ductility, quenching and performance and cracking, so quenching is extremely important, and the tempering must be quenched to avoid the occurrence of temper brittleness.
Normalizing temperature 830 ℃ & 10 ℃, air cooling. Quenching temperature 830 ℃ & 10 ℃, water, oil cooling. Tempering temperature 600 ℃ 10 ℃, water, oil cooling
Desmond does not deliver or heat treatment (annealing, normalizing or high temperature tempering) delivery. Require delivery of heat treatment status should be indicated in the contract.
Other regions Similar grades: DIN: 1.1213, DIN: Cf53, AFNOR: XC48TS, AISI: 1050, JIS: S50C / S53C, GB:
50 steel.
Suitable for manufacturing wear parts with high wear resistance and dynamic impact, such as forged gears, shaft friction discs, machine tool spindles, engine spindles, rollers, drawbars, spring washers, agricultural digging plow, heavy load Axis and so on
1050
Chemical Composition(%)max
C
Si
Mn
Ni
Cr
Cu
0.47-0.55
0.17-0.37
0.50-0.80
0.3
0.15
0.25
Processing:
Shaft parts of the rough: shaft parts according to the use of requirements, production types, equipment conditions and structure, the choice of bar, forgings and other blank form. For the diameter of the outer diameter of the shaft is not the main difference, the general bar to the main; and for the outer diameter of the large difference between the step shaft or important shaft, often use forging, which saves material and reduce the workload of machining, but also Improve mechanical properties. According to the different scale of production, rough forging for free forging and forging two. Small and medium-sized production more free forging, a large number of large-scale production using forging. The following are the same as the "
Shaft parts of the material: shaft parts should be based on different working conditions and the use of different requirements and the use of different heat treatment specifications (such as quenching and tempering, quenching, etc.) to obtain a certain strength, toughness and wear Sex. Fencrole 1050 steel is a common material for shaft parts, it is cheap after quenching and tempering (or normalizing), can get better cutting performance, and can get a higher strength and toughness and other comprehensive mechanical properties, quenched surface Hardness up to 45 ~ 52HRC.
Metallographic organization: pearlite + ferrite.
US Fencor Finkl 1050 carbon tool steel, using electric furnace, flat furnace or pure oxygen converter steelmaking made of the whole static steel, with the characteristics of uniform microstructure. The steel has a carbon content of 0.4%, excellent wear resistance, reduced ductility, quenching and performance and cracking, so quenching is extremely important, and the tempering must be quenched to avoid the occurrence of temper brittleness.
Normalizing temperature 830 ℃ & 10 ℃, air cooling. Quenching temperature 830 ℃ & 10 ℃, water, oil cooling. Tempering temperature 600 ℃ 10 ℃, water, oil cooling
Desmond does not deliver or heat treatment (annealing, normalizing or high temperature tempering) delivery. Require delivery of heat treatment status should be indicated in the contract.
Other regions Similar grades: DIN: 1.1213, DIN: Cf53, AFNOR: XC48TS, AISI: 1050, JIS: S50C / S53C, GB:
50 steel.