316/316L stainless steel chemical composition |
||||||||||
Grade |
C |
Si |
Mn |
Cr |
N |
P |
S |
Ni |
Mo |
Ti |
316 |
≤0.08 |
≤1.00 |
≤2.00 |
16.00~18.50 |
- |
≤0.035 |
≤0.03 |
10.00~14.00 |
2.00~3.00 |
- |
316l |
≤0.03 |
≤0.75 |
≤2.00 |
16.00~18.00 |
- |
≤0.045 |
≤0.03 |
10.00~14.00 |
2.00~3.00 |
- |
316/316L stainless steel physical properties |
||
316 |
Heat Treatment : |
1010~1120 rapid cooling |
Tensile Strength: |
σb (MPa)≥520 |
|
Yield strength : |
σ0.2 (MPa)≥205 |
|
Elongation: |
δ5 (%)≥40 |
|
HBS: |
≤187 |
|
HRB: |
≤90 |
|
HV: |
≤200 |
|
|
||
316l |
Tensile Strength: |
σb (MPa)≥485 |
Yield strength : |
σ0.2 (MPa)≥170 |
|
Elongation: |
δ5 (%)≥30 |
|
Hardness : |
HRB<90 HV<200 HBS<187 |
|
Density : |
7.93g/cm3 |
|
reduction of area: |
ψ (%)≥40 |