Experienced supplier of 1.4404 stainless steel,S31603 stainless steel pipe,316L Stainless Steel

316L/S31603/SUS 316L Stainless Steel

Parameter

Alloy 316L is molybdenum-bearing austenitic stainless steel. The higher nickel and molybdenum content in this grade allows it to demonstrate better overall corrosion resistant properties than 304, especially with regard to pitting and crevice corrosion in chloride environments. In addition, Alloy 316L provides excellent elevated temperature tensile, creep and stress-rupture strengths, as well as outstanding formability and weldability. 316L is the lower carbon version of 316 and is immune from sensitization; therefore, it is very frequently used in heavy gauge welded components.

AISI 316L(1.4404, 1.4432, 1.4435 sS31603)

STANDARDS
INDUSTEEL TRADEMARKS		UNS	ASTM	EURONORMS EN	SUS
316L		S31603	316L	1.4404 X2CrNiMo17-12-2	SUS 316L
CHEMICAL ANALYSIS (%WEIGHT)
C	Cr	Ni	Mo	N	Others
< 0,030	17	10,5	2,1	-

Type	316L stainless steel pipe/tube/plate/sheet/coil
Thinckness	1-30mm
Outer diameter	6-630mm
Length	6m or as customer's requirement
Finish	Polished, Pickled,hairline,mirror
Shap	Round,square, rectangular,oval
Technology	Seamless,weld
Standard	JIS, AISI, ASTM, GB, DIN, EN ,etc.
MOQ	2 Ton
Application	decoration, industry, etc.
Certificate	SGS，ISO9001, MSDS
Packaging	Standard exporting packing

PROPERTIES
0,2 Y.S. - Rp 0,2min ASTM / EN		0,2 Y.S. - Rp 0,2(2)typical value		UTS - Rm min ASTM / EN		UTS - Rm(2)typical value		EI-A(1)%	PREN(4)	HOMOLOGATIONS
MPa	Ksi	MPa	Ksi	MPa	Ksi	MPa	Ksi			Last revised
220	32	295	43	520	75	580	84	45	24	-

Application

APPLICATIONS
CHEMICAL INDUSTRIES			PROCESS INDUSTRIES			WATER TREATMENT			STORAGE & TRANSPORTATION
Nitric Acid	Sulfuric Acid	Polymer& otheracids	Fertilisers	Pulp& Paper	Hydrome-tallurgy	Seawater& desalination	Freshwater &Tanks	Waste Water	Chemical Tanks	Cryogenic Tanks	Renewable

POWER GENERATION				OIL & GAS			CONSTRUCTION
Nuclear	Pollution control	Hydroelectric	Renewable	Off & Onshore & production	Refining & Gas processing	Petrochemical	Architecture	Bridges

For more technical details :
(1) Indicative typical values
(2) Indicative typical values for thickness 20 mm at RT for transverse direction
(3) Hardening 496°C (925°F), 4h, air cooling
(4) PREN = Cr + 3.3 Mo + 16N
(5) PRENW = Cr + 3.3(Mo + 0.5W) + 16N
(6) HT: mechanical properties depend on heat treatment