Description
A prehardened structure(300 HB/30 HRC) and corrosion resistant mold steel
W1.2316 is a 16%Cr 1% Mo with improved corrosion resistance properties, thanks to the chromium and molybdenum additions. The high cleanliness/homogeneity of the steel makes it specially adapted to fine polishing (mirror finish). This steel is commonly used for mold steel applications including cores, inserts, mold cavities… working or stored in wet environments. This grade is also used for the production of corrosive materials like PVC.
Standard
• EN: X36 CrMo17 (S)
• WERKSTOFF Nb: 1.2316
• AFNOR: Z40 CD16S
Parameter
Chemical Analysis
Typical values (weight%).
C
|
S max
|
P max
|
Si
|
Mn
|
Cr
|
Mo
|
0.4
|
0.005
|
0.030
|
0.350
|
0.90
|
16
|
1.03
|
Mechanical Properties
Typical values – th 60 mm – 2.4”: Plates Air quenched and tempered.
Hardness
|
YS 0.2
|
UTS
|
Elongation
|
Reduction
of area
|
KCV
|
Elastic modulus
|
HB
|
MPa
|
ksi
|
MPa
|
ksi
|
%
|
Z%
|
J
|
ft. lbs
|
GPa
|
ksi
|
300
|
855
|
124
|
1020
|
148
|
13
|
38
|
16
|
12
|
205
|
29745
|
340
|
950
|
138
|
1135
|
165
|
10
|
30
|
10
|
8
|
205
|
29745
|
Delivery Conditions
Typical delivery sizes
Thickness
|
Width
|
20 – 120 mm
(.79″ – 4.7″)
|
1500 – 2500 mm
(59 – 98.4″)
|
120 – 300 mm
(4.7″ – 11.8″)
|
1500 – 1700 mm
(49″ – 66.9″)
|